AISI 316L Stainless steel wire rope Corrosion resistant in a variety of marine and chemical environments and excellent corrosion resistance,weight
C% | Si% |
Mn% |
P% |
S% |
Cr% |
Ni% |
N% |
Mo% |
Ti% |
|
≤0.08 |
≤0.75 |
≤2.0 |
≤0.045 |
≤0.03 |
16.0-18.0 |
10.0-14.0 |
-- |
2.0-3.0 |
-- |
T*S |
Y*S |
Hardness |
Elongation |
|
(Mpa) |
(Mpa) |
HRB |
HB |
(%) |
≥520 |
≥205 |
-- |
-- |
≥4 |
Product |
Stainless Steel Wire Rope |
Size |
1x3/1x7/1x19/3x7/6x7/6x19 etc. |
Length |
Unlimited or as customer decided |
Finish |
Cloudy,Bright,Pickled,Mill,Mat |
Standard |
ASME, ASTM, EN ,BS,GB,DIN, JIS etc |
Material |
201,202,302,303,303se,304,304L,304H,308,309,310,310s |
Hardness |
all soft |1/4 hard|semi-hard|3/4 hard|full hard|ultra hard. |
Package |
Plywood reels, plastic spools or according to requirements.Wooden box |
Surface |
Construction |
Diameter (mm) |
Tensile Strength |
Bright |
1x7 |
0.6--14 |
1270N/mm2--1960N/mm2 |
1x19 |
1.0--8.0 |
||
1x12 |
1.0--8.0 |
||
7x7 (6x7+IWRC) |
1.0--20 |
||
6x19+IWRC |
3.0--56 |
||
6x19W/S+IWRC |
6.0--38 |
||
6x37+IWRC |
6.0--64 |
||
6x19/25Fi+IWRC |
6.0--44 |
||
8x19S/W+IWRC |
8.0--16 |
||
8x19S+IWRC |
8.0--16 |
||
6x36WS+IWRC |
8.0--56 |
||
19x7 |
4.0--28 |
||
6x19+FC |
3.0--56 |
||
6x19W/S+FC |
6.0--36 |
||
6x37+FC |
6.0--64 |
||
6x19Fi+FC |
6.0--44 |
||
8x19S/W+FC |
8.0--16 |
||
8x19S+FC |
6.0--16 |
||
6x36WS+FC |
8.0--56 |
||
6x24+7FC |
6.0--56 |
||
6x12+7FC |
3.0--32 |
||
18x7+FC |
4.0--28 |
construction |
dia(mm) |
tolerance |
Appro Weight(kg/100m) |
MBL/KN |
1*7 |
0.3 |
0/+0.08 |
0.05 |
0.075 |
0.4 |
0.08 |
0.133 |
||
0.6 |
0.18 |
0.3 |
||
0.8 |
0.32 |
0.533 |
||
1 |
0.51 |
0.832 |
||
1.2 |
0.73 |
1.198 |
||
1.5 |
1.14 |
1.872 |
||
1.8 |
1.64 |
2.696 |
||
2 |
2.02 |
3.325 |
||
2.5 |
3.16 |
5.201 |
||
3 |
4.55 |
7.489 |
||
4 |
0/+0.07 |
8.08 |
13.314 |
|
1*19 |
0.8 |
0/+0.08 |
0.31 |
0.53 |
1 |
0.49 |
0.82 |
||
1.5 |
1.11 |
1.85 |
||
1.8 |
1.6 |
2.67 |
||
2 |
1.98 |
3.3 |
||
2.5 |
3.09 |
5.16 |
||
3 |
4.45 |
7.43 |
||
4 |
0/+0.07 |
7.92 |
13.21 |
|
5 |
12.37 |
20.64 |
||
6 |
0/+0.06 |
17.82 |
29.72 |
|
8 |
0/+0.05 |
31.68 |
52.85 |
|
10 |
49.6 |
82.58 |
||
12 |
71.28 |
118.91 |
||
1*37 |
5 |
0/+0.07 |
12.23 |
20.41 |
6 |
0/+0.06 |
17.6 |
29.39 |
|
8 |
0/+0.05 |
31.3 |
52.25 |
|
10 |
48.9 |
81.64 |
||
12 |
70.42 |
117.56 |
||
14 |
95.84 |
160.01 |
||
16 |
125.18 |
208.99 |
||
18 |
158.44 |
264.51 |
||
20 |
195.6 |
326.56 |
||
7*7 |
0.33 |
0.037 |
0.1 |
|
0.36 |
0/+0.08 |
0.054 |
0.15 |
|
0.5 |
0.09 |
0.14 |
||
0.8 |
0.25 |
0.29 |
||
1 |
0.39 |
0.56 |
||
1.2 |
0.56 |
0.81 |
||
1.5 |
0.88 |
1.27 |
||
1.8 |
1.27 |
1.83 |
||
2 |
1.57 |
2.25 |
||
2.5 |
2.45 |
3.52 |
||
3 |
3.53 |
5.07 |
||
4 |
0/+0.07 |
6.28 |
9.01 |
|
5 |
9.82 |
14.09 |
||
6 |
0/+0.06 |
14.14 |
20.29 |
|
8 |
0/+0.05 |
25.15 |
36.07 |
|
10 |
39.3 |
56.36 |
||
12 |
56.59 |
81.16 |
||
7*19 |
1.2 |
0/+0.08 |
0.54 |
0.75 |
1.5 |
0.85 |
1.17 |
||
1.8 |
1.23 |
1.68 |
||
2 |
1.52 |
2.08 |
||
2.5 |
2.38 |
3.25 |
||
3 |
3.42 |
4.69 |
||
4 |
0/+0.07 |
6.09 |
8.33 |
|
5 |
9.52 |
13.03 |
||
6 |
0/+0.06 |
13.71 |
18.76 |
|
7 |
18.66 |
25.54 |
||
8 |
0/+0.05 |
24.38 |
33.35 |
|
10 |
38.1 |
52.12 |
||
12 |
54.86 |
75.05 |
||
14 |
74.67 |
102.16 |
||
16 |
97.53 |
133.43 |
||
18 |
123.44 |
168.88 |
||
20 |
152.4 |
208.49 |
||
24 |
219.45 |
300.23 |
||
26 |
257.55 |
352.35 |
||
6*19S/W+IWRC |
8 |
0/+0.05 |
25.92 |
35.77 |
10 |
40.5 |
55.89 |
||
12 |
58.32 |
80.48 |
||
14 |
79.38 |
109.55 |
||
16 |
103.68 |
143.08 |
||
18 |
131.22 |
181.09 |
||
20 |
162 |
223.57 |
||
6*36S/W+IWRC |
8 |
0/+0.05 |
26.75 |
35.77 |
10 |
41.8 |
55.89 |
||
12 |
60.19 |
80.48 |
||
14 |
81.93 |
109.55 |
||
16 |
107.01 |
143.08 |
||
18 |
135.43 |
— |
||
20 |
167.2 |
— |
||
22 |
202.31 |
— |
||
24 |
240.77 |
— |
||
26 |
282.57 |
— |
||
28 |
327.71 |
— |
||
19*7 |
4 |
0/+0.07 |
6.43 |
7.61 |
5 |
10.05 |
13.58 |
||
6 |
0/+0.06 |
14.47 |
19.56 |
|
7 |
19.69 |
26.62 |
||
8 |
0/+0.05 |
25.73 |
34.77 |
|
10 |
40.2 |
54.32 |
||
12 |
57.89 |
78.22 |
||
14 |
78.79 |
106.47 |
||
16 |
102.91 |
139.06 |
||
18 |
130.25 |
176 |
||
20 |
160.8 |
217.29 |
Type AISI |
C Max % |
Mn Max % |
P Max% |
S Max% |
Si Max% |
Cr% |
Ni% |
Mo% |
201 |
0.15 |
5.50-7.50 |
0.06 |
0.03 |
1 |
16.000-18.00 |
0.5 |
- |
202 |
0.15 |
7.50-10.00 |
0.06 |
0.03 |
1 |
17.00-19.00 |
3.-0-5.00 |
- |
204CU |
0.08 |
6.5-8.5 |
0.06 |
0.03 |
2 |
16.0-17.0 |
1.5-3.0 |
- |
302 |
0.15 |
2 |
0.045 |
0.03 |
1 |
17.00-19.00 |
8.00-10.00 |
- |
302HQ/ |
0.03 |
2 |
0.045 |
0.02 |
1 |
17.00-19.00 |
9.00-10.00 |
- |
304CU | ||||||||
304HC |
0.04 |
0.80-1.70 |
0.04 |
0.015 |
0.3-0.6 |
18-19 |
8.5-9.5 |
- |
303 |
0.07 |
2 |
0.045 |
0.25 Min |
1 |
17-19 |
8.0-10.0 |
0.6 |
304 |
0.08 |
2 |
0.045 |
0.03 |
1 |
18.00-20.00 |
8.0-10.50 |
- |
304L |
0.03 |
2 |
0.045 |
0.03 |
1 |
18.00-20.00 |
8.00-12.00 |
- |
310 S |
0.055 |
1.5 |
0.04 |
0.005 |
0.7 |
25.0-28.0 |
19-22 |
- |
314 |
0.25 |
2 |
0.045 |
0.03 |
1.50-3.00 |
23.00-26.00 |
19.00-22.00 |
- |
316 |
0.06 |
2 |
0.045 |
0.03 |
1 |
16.00-18.00 |
10.00-14.00 |
2.00-3.00 |
316L |
0.03 |
2 |
0.045 |
0.03 |
1 |
16.00-18.00 |
10.00-14.00 |
2.00-3.00 |
316Ti |
0.08 |
2 |
0.045 |
0.03 |
0.75 |
16.00-18.00 |
10.00-14.00 |
2.00-3.00 |
347 |
0.08 |
2 |
0.045 |
0.03 |
1 |
17.00-19.00 |
9.00-13.00 |
- |
321 |
0.06 |
2 |
0.045 |
0.01 |
.40-.60 |
17-19.00 |
9.4-9.6 |
- |
SASA METAL, established in 1995, is an experienced and professional manufacturers and suppliers of 316 stainless steel wire rope. With the aid of qualified workers and advanced equipment, we can assure you the high quality and good performance of our products. Please be free to buy products for sale with us.